ADVANTAGES
- Easy to apply and to level
- High mechanical properties, good elongation
- Catalyst revelator included
- High thixotropy, allowing application of big thickness onvertical parts without sagging
- Low shrinkage, minimum print through
- Excellent adhesion of Polyester laminates,wood/polyester, Omega bonding.
- Used in the Marine, Swimming pools, Transport andindustrial applications
TECHNICAL SPECIFICATIONS
|
Static viscosity (poises) |
15 000 – 20 000 |
|
Thixotropy |
≥ 5,5 |
|
Density |
1,33 ±0,05 |
|
Geltime (min) * |
25 – 40 min |
|
Cure time (min) |
50 – 80 min |
- *Reactivity on 200g mass , with 2% PMEC 50, at 20°C
Mechanical Properties of the base resin:
|
Flexural strength |
( MPa ) |
116 |
EN ISO 178 |
|
Flexural modulus |
( MPa ) |
3801 |
EN ISO 178 |
|
Flexural elongation at break |
(%) |
4,1 |
EN ISO 178 |
|
Tensile strength |
( MPa ) |
65 |
EN ISO 527 |
|
Tensile modulus |
( MPa ) |
2955 |
EN ISO 527 |
|
Tensile elongation at break |
(%) |
2,9 |
EN ISO 527 |
|
HDT |
( °C ) |
64 |
EN ISO 75-2 |
APPLICATION
This product must be used at workshop temperature between 15 and 30°C.
Catalyze: between 1 and 2 % of MEKP 50, according to the requested thickness and production cycle.
Material bonding on laminate
The surface must be free from any contamination and should not be coated with paraffin. All organic coating such as epoxy, polyurethane or alkyd paints should be removed completely.
The laminate must be minimum in gel.
Prepare and add the catalyst.
The catalyst revelator enables to check the quality of the mixing.
Depending of the storage time and temperature, the gel time can change. In that case it is possible to increase the catalyst level up to 3%.
Application with spatula, pastry bag and suitable bonding machines.
We do not recommend application with less than 10°C ( air and surface temperature )
Please contact us for further information.
STORAGE CONDITIONS
Product should be kept away from direct sunshine and at temperature below 20°C. Under these conditions, the product will keep its properties 4 months from production date.
The information contained in this technical data sheet reflects our current knowledge. It aims at providing information about the application possibilities.
As we cannot control the applications’ conditions, we cannot be held as responsible beyond the providing of material in accordance with our specifications.