ADVANTAGES
- Easy to apply and to level
- High mechanical properties
- Catalyst revelator included
- High thixotropy, allowing application of big thickness onvertical parts without sagging
- Easy positioning of cores in sandwich structures
- Low shrinkage
- Semi-flexible
- Excellent adhesion of core materials (balsa, foam…)
- Also suitable as a bonding paste for other materials
TECHNICAL SPECIFICATION
|
Ref. |
FSP-HV 1537 |
|
Static viscosity (cps) |
450 000 – 600 000 |
|
Thixotropy |
7 |
|
Density |
1.3 ± 0.05 |
|
Gel time (minutes) * |
40 – 60 |
|
Gel time (minutes) ** |
15 – 30 |
|
Full cure |
After 3 hours |
- * Reactivity of 100 gr mass with 1% PMEC 50 at 20°C
- ** Reactivity of 100 gr mass with 2% PMEC 50 at 20°C
TYPICAL MECHANICAL PROPERTIES
|
Flexural strengh |
( MPa ) |
126 |
EN ISO 178 |
|
Flexural elasticity modulus |
( MPa ) |
3591 |
EN ISO 178 |
|
Flexural elongation at break |
4.5% |
EN ISO 178 |
|
|
Tensile strengh |
( MPa ) |
59 |
EN ISO 527 |
|
Tensile elasticity modulus |
( MPa ) |
3350 |
EN ISO 527 |
|
Tensile elongation at break |
2.7% |
EN ISO 527 |
|
|
HDT |
( °C ) |
61 |
EN ISO 75-2 |
APPLICATION
This product must be used at workshop temperature between 15 and 30°C.
Catalyze: between 0.6 and 2.0 % of MEKP 50, according to the requested thickness and production cycle.
Core material bonding on laminate
The surface must be free from any contamination and should not be coated with paraffin. All organic coating such as epoxy, polyurethane or alkyd paints should be removed completely.
The laminate must be minimum in gel. Prepare and add the catalyst.
The catalyst revelator enables to check the quality of the mixing.
Apply the requested thickness (max. 20mm), with a paste spatula.
Apply the core on the paste and press to spread the FSP and chase the air…
STORAGE CONDITIONS:
Product should be kept away from direct sunshine and at temperature below 20°C. Under these conditions, the product will keep its properties 4 months from production date.
The information contained in this technical data sheet reflects our current knowledge. It aims at providing information about the application possibilities.
As we cannot control the applications’ conditions, we cannot be held as responsible beyond the providing of material in accordance with our specifications.